Made from pure virgin PTFE resin, it features good flexibility peculiarity, encapsulate resilience, resistant high & low Temperature and excellent resistant corrosion, no aging, lubrication itself.
Application: Used in practically every type of sealing application, and it is ideal for sealing complex surfaces and rough or pitted flanges.
Recommended For: all common chemicals in 0-14 ph range except molten alkali metals and elemental fluorine
Limitations: Temperatures to 300°C, pressures to 20 Mpa.
Specification:
JJ-TS3001 Expanded PTFE Joint Sealant
Size:3-100mm (W)×1-10mm (T)×L(based on your request)
Technical parameter
|
Index
|
Unit
|
Standard
|
|
Apparent Density
|
g/cm3
|
0.75
|
|
Tensile Strength
|
Mpa
|
≥8.0
|
|
Volatile content
|
%
|
≤1.0
|
|
Hardness
|
HA
|
30~70
|
|
Creep Relaxation
|
%
|
≤40
|
|
Working Temperature
|
°C
|
-100~280
|
|
Working Pressure
|
Mpa
|
Gas
1.6
|
|
Liquid
6.4
|
|
PH Range
|
|
0~14
|
|
Stretch Pressure
|
MPa
|
Min8~20(3mm~25mm)
|
|
Moisture Content
|
%
|
≤0.01
|
|
Melting Point
|
°C
|
327
|
|
Thermal-labile Index
|
index
|
10
|
|
Average Particle Size
|
μm
|
500
|
General Size & Packaging Standard
|
Size
|
Spool
length
|
|
Width(mm)
|
Thickness(mm)
|
|
3.0
|
1.5
|
30.0
|
|
3.0
|
2.0
|
30.0
|
|
4.0
|
2.0
|
30.0
|
|
5.0
|
3.0
|
25.0
|
|
5.0
|
2.0
|
25.0
|
|
7.0
|
2.5
|
20.0
|
|
7.0
|
3.0
|
20.0
|
|
8.0
|
3.0
|
10.0
|
|
9.0
|
4.0
|
10.0
|
|
10.0
|
3.0
|
20.0
|
|
10.0
|
4.0
|
10.0
|
|
12.0
|
4.0
|
6.0
|
|
14.0
|
5.0
|
6.0
|
|
16.0
|
5.0
|
3.0
|
|
Size
|
Spool length
|
|
Width(mm)
|
Thickness(mm)
|
|
17.0
|
6.0
|
30.0
|
|
20.0
|
7.0
|
30.0
|
|
22.0
|
7.0
|
30.0
|
|
25.0
|
8.0
|
25.0
|
|
28.0
|
5.0
|
25.0
|
|
30.0
|
5.0
|
20.0
|
|
40.0
|
4.0
|
20.0
|
|
50.0
|
4.0
|
10.0
|
|
60.0
|
3.0
|
10.0
|
|
70.0
|
3.0
|
20.0
|
|
80.0
|
2.5
|
10.0
|
|
100.0
|
0.4
|
6.0
|
|
100.0
|
0.5
|
6.0
|
|
100.0
|
1.0
|
3.0
|
|